A team of researchers recently published a paper in the journal ACS Energy Letters that demonstrated a new entirely photostimulation-induced reversible photochromic glass for three-dimensional (3D) optical storage applications.
Study: Entirely Reversible Photochromic Glass with High Coloration and Luminescence Contrast for 3D Optical Storage . Image Credit: Gorodenkoff/Shutterstock.com
The significant growth of digital information in the modern era has necessitated the development of high-density storage media and optical storage technologies. Although several new optical storage technologies, such as multiwavelength optical storage, holographic optical storage, super-resolution optical storage, and near-field optical storage, have been developed, these technologies require sophisticated manipulation and expensive equipment, which restricted their use in many practical applications.
Photochromism has gained significant attention as an effective optical storage technology. The phenomenon is described as the photostimulation-induced reversible color change of materials. Currently, photochromic ceramics and thin films are used extensively for optical storage applications. However, these two-dimensional (2D) photochromic storage media lack high storage capacity as the optical information is only recorded on their surface.
The integration of multiple dimensions such as luminescence, phase, wavelength, and space into a single optical carrier can potentially increase the storage capacity. Glass, a versatile material with good transparency, is considered a suitable alternative for multidimensional optical storage applications. Thus, a high optical storage capacity can be achieved in photochromic glass in 3D bulk dimensions.
Lanthanide (Ln) ion-doped luminescent glasses have demonstrated significant potential for applications in the fields of nonlinear optics, energy storage, 3D displays, solid-state lasers, and optical communication. Recently, the luminescence in Ln-ion doped glasses was modulated successfully. For instance, the optical storage application and luminescence modification were achieved through the transformation of the valence state from samarium (III) ion (Sm3+) to Sm2+ when an Sm3+ -doped glass was illuminated using an 800 nm femtosecond laser.
Double-model rewritable optical storage can be realized by integrating luminescence modification and photochromism into a bulk glass. Thus, photochromic glasses with luminescence modification can potentially act as an alternative optical storage media.
For instance, a rare earth (RE) ion-doped photochromic tungsten phosphate glass demonstrated a 3D optical storage capacity and information encryption based on the reversible transformation of valence state from tungsten ion (W6+) to W5+. However, the glass was bleached using thermal stimulation, which restricted its applications. Thus, a completely photostimulation-induced reversible photochromic glass could be an attractive option for 3D optical storage applications as it does not require thermal treatment.
In this study, researchers synthesized an entirely photostimulation-induced reversible photochromic germanium borate glass doped with (RE-Ag) using the conventional melt-quenching method. The reversible photochromism mechanisms of the synthesized RE-Ag germanium borate glass were thoroughly evaluated under alternating simulation between a 690 nm laser light and 365 nm ultraviolet (UV) light by determining the decomposition and formation of Ag nanoparticles in the RE-Ag germanium borate glass host.
Dysprosium (III) oxide, europium (III) fluoride, AgCl, cuprous oxide, strontium carbonate, zinc oxide, boron trioxide, aluminum oxide, silicon dioxide, and germanium dioxide were used as raw materials to prepare Ag- and RE ions/dysprosium ion (Dy3+) or europium ion (Eu3+) ion-doped germanium borate glasses.
Initially, the raw materials were weighed, mixed, and ground using an agate mortar. Then, the obtained mixtures were melted at 1300 °C for 30 min in an alumina crucible under an ambient atmosphere.
Subsequently, the glass melt was transferred to a stainless-steel container preheated at 350 °C and left undisturbed for 20 min. The as-prepared bulk glasses were then heat-treated for one h at 600 °C to crystallize AgCl nanocrystals. The rectangular glass was finally obtained by grinding and polishing.
An X-ray diffractometer, transmission electron microscope with energy dispersive X-ray spectrometer, X-ray photoelectron spectroscope, infrared spectrometer, paramagnetic resonance spectrometer, Hitachi F-7000 spectrophotometer using a xenon (Xe) lamp as the light source, and an Edinburgh FLS 980 instrument were used to characterize the synthesized glass.
Researchers successfully synthesized an entirely photostimulation-induced reversible photochromic RE-Ag germanium borate glass. The germanium borate glass possessed a high defect tolerance and a less rigid environment, which was beneficial for the AgCl nanocrystal precipitation from borosilicate glasses. The photostimulation-induced reversible color change was attributed to the decomposition and precipitation of Ag microcrystals in the glass host.
Intricate optical information patterns were erased and written in the photostimulated glass by alternating a 690 nm laser and 365 nm UV light. An optical information readout was realized after the UV light irradiation by exciting the glass using an excitation light from a Xe lamp.
Both luminescence modulation and photochromic behavior properties demonstrated high repeatability and fatigue resistance. The change of the Ag element valence state was primarily responsible for the photochromic mechanism. The Ag nanoparticle precipitation due to UV light irradiation induced darkening of the glass.
In the Eu3+-doped germanium borate (Eu-Ag) glass, the reversible downshifted luminescence modification was attained due to decolorization and photochromism. The reversible photochromism/coloration contrast from transparent to black and luminescence modulation was 91% and 93%, respectively, when the glass was alternatively irradiated by 365 nm UV light and 690 nm laser light for 30 s.
Taken together, the findings of this study demonstrated that the synthesized photostimulation-induced AgCl and RE-ion doped photochromic glass possesses a significant potential for information encryption and storage applications.
More from AZoM: Use and Applications of Flame Atomic Absorption Spectroscopy
Liao, J., Xiao, D., Zhao, H. et al. Entirely Reversible Photochromic Glass with High Coloration and Luminescence Contrast for 3D Optical Storage. ACS Energy Letters 2022. https://doi.org/10.1021/acsenergylett.2c00574
Disclaimer: The views expressed here are those of the author expressed in their private capacity and do not necessarily represent the views of AZoM.com Limited T/A AZoNetwork the owner and operator of this website. This disclaimer forms part of the Terms and conditions of use of this website.
Samudrapom Dam is a freelance scientific and business writer based in Kolkata, India. He has been writing articles related to business and scientific topics for more than one and a half years. He has extensive experience in writing about advanced technologies, information technology, machinery, metals and metal products, clean technologies, finance and banking, automotive, household products, and the aerospace industry. He is passionate about the latest developments in advanced technologies, the ways these developments can be implemented in a real-world situation, and how these developments can positively impact common people.
Please use one of the following formats to cite this article in your essay, paper or report:
Dam, Samudrapom. (2022, May 27). Information Encryption and 3D Optical Storage in Glass. AZoM. Retrieved on May 27, 2022 from https://www.azom.com/news.aspx?newsID=59184.
Dam, Samudrapom. "Information Encryption and 3D Optical Storage in Glass". AZoM. 27 May 2022. <https://www.azom.com/news.aspx?newsID=59184>.
Dam, Samudrapom. "Information Encryption and 3D Optical Storage in Glass". AZoM. https://www.azom.com/news.aspx?newsID=59184. (accessed May 27, 2022).
Dam, Samudrapom. 2022. Information Encryption and 3D Optical Storage in Glass. AZoM, viewed 27 May 2022, https://www.azom.com/news.aspx?newsID=59184.
Do you have a review, update or anything you would like to add to this news story?
In this interview, AZoM talks to Chris Aylott, Senior Engineer at Newcastle University, about fatigue testing in the development of low carbon transport solutions.
AZoM speaks with Dr. Nicola Ferralis from MIT about his research that has developed a low-cost process of creating carbon fibers from hydrocarbon pitch. This research could lead to the large-scale use of carbon fiber composites in industries that have thus far been limited.
In this interview, AZoM speaks with Marco Enger, Senior Tribologist from GGB, to discuss how nano fillers affect transfer films within tribological systems.
This product profile outlines the Versa Flex Checkweighers from Thermo Fisher Scientific.
The LQA 300 FT-IR wine analyzer combines performance, accuracy, ease-of-use, and speed for the analysis of finished wine, must and must under fermentation samples in less than 45 seconds—all in one compact solution.
The SpectraStar™ XT-R Benchtop NIR can analyze virtually any sample type in less than a minute, including solid, slurry, or liquid samples.
This article provides an end-of-life assessment of lithium-ion batteries, focusing on the recycling of an ever-growing amount of spent Li-Ion batteries in order to work toward a sustainable and circular approach to battery use and reuse.
Corrosion is the degradation of an alloy caused by its exposure to the environment. Corrosion deterioration of metallic alloys exposed to the atmosphere or other adverse conditions is prevented using a variety of techniques.
Due to the ever-increasing demand for energy, the demand for nuclear fuel has also increased, which has further created a significant increase in the requirement for post-irradiation examination (PIE) techniques.
AZoM.com - An AZoNetwork Site
Owned and operated by AZoNetwork, © 2000-2022